Header for module of hollow fiber membranes and method of potting hollow fibers

ABSTRACT

Hollow fiber membranes are potted by injection molding a thermoplastic material into a cavity containing the fibers. The cavity is formed in part by the interaction of a mold and a layer of an adhesive pre-applied to a bundle of the membranes.

This is an application claiming the benefit under 35 USC 119(e) of U.S.Application Ser. No. 60/623,540 filed Oct. 28, 2004. Application Ser.No. 60/623,540 is incorporated herein, in its entirety, by thisreference to it.

FIELD

This specification may relate to methods of potting hollow fibermembranes, to methods of making headers for modules of hollow fibermembranes, to potted hollow fiber membranes or to headers or modules ofpotted hollow fiber membranes.

BACKGROUND

The following description does not admit or imply that the apparatus ormethod discussed below is citable as prior art or part of the generalknowledge of a person skilled in the art in any particular country.

In order to filter or permeate with hollow fibre membranes, a largenumber of thin hollow fibres must be fixed to a header such that theirouter surfaces are each completely sealed to the outside of the headerbut their lumens are open to an inner space in the header. The innerspace of the header is then connected to a source of suction or pressureto create a transmembrane pressure across the walls of the membranes andcarry fluids to or from the lumens of the membranes.

In U.S. Pat. No. 5,639,373, the ends of an array of fibres are submergedin a fugitive liquid, such as a wax, until the fugitive liquidsolidifies around them. A fixing liquid, such as a resin, is then pouredover the fugitive liquid and allowed to harden around the membranes. Thefugitive liquid is then removed, for example by heating or bydissolution, leaving the lumens of the membranes open to the spaceformerly occupied by the fugitive liquid. In U.S. Pat. No. 6,042,677, asimilar process is used but the array of fibres is held in a bed ofpowder which is used in place of the solidified fugitive liquid.

In U.S. Pat. No. 5,922,201, a continuous hollow fibre is made into afabric such that adjacent lengths of the fibres are spaced apart fromeach other and do not have open ends. An edge of the fabric is insertedinto a pot of liquid resin which is centrifuged or vibrated as it curesto encourage flow into the spaces between the fibres. After the resin iscured, the block of resin and fibre is cut to separate the fabric intoindividual lengths of fibres having open ends. The block of resin isthen glued or attached through gaskets to the remainder of a header.

In European Patent Application No. EP 0 931 582, an elastic pipe is usedto make a header. An aperture is cut in the pipe and a weir is built uparound the aperture. Open ends of hollow fibre membranes are insertedinto the aperture by first pulling the aperture open and then allowingit to close on the membranes. Liquid resin is poured over the ends ofthe membranes and retained in placed by the weir until it cures. Surfacetension prevents the resin from flowing through the aperture in spacesbetween adjacent fibres.

SUMMARY

The following summary is intended to introduce the reader to thespecification, but not to define the invention. The invention orinventions may reside in a combination or sub-combination of featuresfound in this summary or in other parts of this document, for examplethe claims.

The inventors have observed various difficulties with prior art pottingmethods. In particular, the use of curable, resinous liquids createsvarious drawbacks. For example, curable materials such as polyurethane,epoxy or silicone are expensive. The time required to cure thesematerials is also long, typically at least 10 minutes and more oftenhours because fast curing of a large block of resin creates excess heat.The resins may also require careful mixing or curing procedures, or mayrelease harmful chemicals as they cure. Wicking of the liquid resin upthe length of the fibers prior to curing can also be a problem.

In a method of potting hollow fiber membranes, the membranes areprovided in a bundle having a layer of a compressible materialsurrounding the membranes in a plane spaced from the ends of themembranes. The layer of compressible material may be formed by placinglayers of hot melt adhesive over sheets of fibers, optionally stackingmultiple sheets of the fibers together. The fibers are then placed in amold which compresses the band of compressible material to form agenerally sealed cavity containing the fibers. A molten potting materialis injected into the cavity to surround the membranes. The pottingmaterial is cooled in the mold and hardens forming a block of solidpotting material sealingly connected to the membranes. Optionally, twospaced-apart layers of compressible material may be provided on thebundle. The mold compresses both layers to provide a cavity between thetwo layers which is filled with injected potting material. In this case,the fixing liquid does not flow to the ends of the membranes whichremain open.

In a method of making a header having potted hollow fiber membranes, amethod as described above is used to pot the membranes into a block ofpotting material. In one method, the potting material is removed fromthe mold and then cut to re-open the ends of the fibers. The block ofpotting material is then sealed to a header pan to form a permeatecollection zone in communication with the fiber ends. In another method,a block of potting material formed between two bands of compressiblematerial is sealed to a header pan with the open ends of the fibers, andthe layer of compressible material closest to them, inside a permeatecollection zone. In another method, a block of potting material isformed between two bands of compressible material while the band ofcompressible material closest to the ends of the membranes is insertedinto a header pan. In this way, the block of potting material is formedin or around, and seals to, the top of the header pan and the membranesat the same time.

In other aspects, the specification describes potted membranes orheaders. In one example, the invention relates to an assembly of pottedmembranes having a band of adhesive, compressible material and a blockof a solidified thermoplastic potting material. In another aspect, theinvention relates to an assembly as described above having the block ofpotting material sealed to a header pan to form a permeate cavity incommunication with ends of the membranes.

BRIEF DESCRIPTION OF THE DRAWINGS

Examples of embodiments of the invention or inventions will be describedbelow with reference to the following figures.

FIG. 1 shows a plan view of a layer of adhesive compressible materialplaced on a sheet of fibers.

FIG. 2 shows an isometric view of sheets of fibers of FIG. 1 assembledinto a larger bundle of fibers having a layer of adhesive, compressiblematerial.

FIG. 3 is a cutaway isometric view of the bundle of FIG. 2 inserted intoa first mold.

FIG. 4 shows a cutaway isometric view of the bundle of FIG. 2 insertedinto a second mold.

FIG. 5 shows a cutaway view of a potted bundle of membranes attached toa header pan.

FIG. 6 is a photograph of a bundle of potted fibers cut through thepotting material.

FIG. 7 is a picture of an assembly of potted membranes.

DESCRIPTION OF EMBODIMENTS

FIG. 1 shows a sheet 10 of hollow fiber membranes 12. The sheet 10 isformed by laying the membranes 12 on a supporting surface, such as atable, so that the membranes 12 are generally parallel to each other butspaced apart from each other, for example from between 0.2 to 2 timestheir diameter, at least in a potting region 14 near their open ends 16.Optionally, the sheet 10 may be formed by any suitable fabric formingmethod and have inert fibers running transversely across the membranes12 to help maintain the membranes 12 in position. Further optionally,the sheet 10 may be formed by winding the membranes 12 onto a drum,preferably through a guide that advances across the face of the drum ata speed, relative to the speed of rotation of the drum, which lays thefibers in a spiral around the drum at a desired spacing. The membranes12 may have diameters, for example, between 0.5 and 2.5 mm and there maybe, for example, between 50 and 400 membranes 12 in a sheet 10. Thewidth of the sheet 10 may be, for example, from 400 mm to 1200 mm andthe length of the sheet 10, and its membranes 12, may be, for example,between 200 and 3200 mm. In various Figures, the membranes 12 are shownas cut to a shorter length to allow other parts to be shown larger.

A first layer 18 of a compressible adhesive 20 is placed over the sheet10 so that the ends 16 of the membranes 12 and the first layer 18 ofadhesive 20 are on opposite sides of the potting region 14. The adhesive20 holds the sheet 10 together. The adhesive 20 also seals to the entireouter circumference of the membranes 12, although a perfect bubble tightseal does not need to be formed. The length, width and thickness of thefirst layer 18 of adhesive 20 are maintained to a size that willcooperate with a mold to be described below. The adhesive 20 may bethermoplastic and applied by first melting it so that it may flow overand around the membranes 12. The adhesive 20 may also be melted afterapplying it to the membranes 12, or molded or shaped while it is moltento provide a layer of more uniform shape or more carefully controlledsize. The adhesive 20 may also be generally soft, so as to be moreeasily compressed into a seal with the mold, as will be described below,and to provide a cushioning layer for the membranes 12. For example, theadhesive 20 may be of a type normally referred to as hot melt glue,which may be a polyethylene or a blend of ethylene vinyl acetateco-polymers. Alternately, the adhesive may be a resin such aspolyurethane or epoxy. Optionally, a second layer 22 of adhesive 20 mayalso be provided in a manner as described for the first layer 18.However, the second layer 22 is applied between the ends 16 and thepotting region 14. The second layer 22 does not cover or fill the ends16 of the membranes 12. However, the second layer 22 is preferablyplaced as close as practical to the ends 16 of the membranes 12 withoutclosing the ends 16 to reduce the length of the membranes 12 that willprotrude into, and interfere with flows of fluids in, the permeatecavity of a finished header.

FIG. 2 shows a bundle 24 of membranes 12 made by stacking a number ofsheets 10, for example between 1 and 30 or between 10 and 20 sheets 10together. The sheets 10 are stacked so that the adhesive layers 18, 22lay on top of each other to generally form a parallelepiped. Optionally,one or more sheets 10 may be rolled up together to generally form acylinder or made into other shapes. The sheets 10 may be glued, weldedor clamped together or simply held together manually or by wrapping astring, wire, band or other wrap around the bundle 24.

FIG. 3 shows the bundle 24 placed into a first mold 30. The mold has afirst plate 32 and a second plate 34 having contact surfaces 36 and moldsurfaces 38. After the bundle 24 is inserted between the plates 32, 34,the plates 32, 34 are brought towards each other by tightening screws,not shown, in screw holes 40. As the plates 32, 34 move together, thecontact surfaces 36 compress the adhesive layers 18, 22 and create atemporary seal. A cavity 44 is formed between the mold surfaces 38 ofthe plates 32, 34, the adhesive layers 18, 22 and ends (not shown) ofthe first mold which contact the ends of the adhesive layers 18, 22. Thepotting region 14 of the bundle 24 is inside of the cavity 44. One ormore inlet nozzles 42 allow molten potting material to be injected intothe cavity 44. One or more ejector pins 46 may be used to get bundle 24out from the cavity 44 after potting and secondarily to permit airventing of the cavity 44. To complete potting the membranes 12, moltenpotting material is injected into the nozzles 42 to fill the cavity 44.The adhesive layers 18, 22 prevent the potting material from leaving thecavity 44. The potting material flows around the bundle 24 and thenpenetrates into the spaces between the membranes 12. The pottingmaterial is then cooled sufficiently quickly to avoid damage to themembranes 12 or excessive melting of the adhesive layers 18, 22. Afterthe potting material hardens, the plates 32, 34 may be moved apart fromeach other to remove the potted bundle 24. The potting material may beone of the several thermoplastic polymers commonly used in injectionmolding, such as Polypropylene (PP), Polyethylene (PE), High DensityPolyethylene (HDPE), moplastic Elastomer (TPE), ThermopasticPolyurethane (TPU), Acrylonitrile Butadiene Styrene (ABS), Polyamide(PA), polystyrene (PS), Polypropylene (PP), Polyethylene Copolymers orPolyolefin based hotmelt polymers or glues, or any of these materials ina filled form, for example glass filled. The membranes 12 may also be ofvarious types of construction known in the art, but must be sufficientlystrong to not be flattened by the injected potting material. Forexample, the membranes 12 may be reinforced fibers having a braidedsupport such as membranes made by ZENON Environmental Inc. for ZEEWEED™500 series modules.

After the potted bundle 24 is removed, it can be attached to a headerpan 52. As shown in FIG. 5, the ends 16 of the membranes 12 are insertedinto the inside of the permeate pan 52 where a permeate (or feed) cavity54 is formed. The potting material 50 is sealed to the walls 56 of theheader pan 52 to close the permeate/feed cavity 54, but for one or moreports 58 in the header pan 52 and the ends 16 of the membranes 12. Theconnection between the permeate pan 52 and the potting material 50 canbe made by various methods such as gluing, welding or mechanicalfasteners, optionally through a gasket or other intermediate material.Further optionally, the potting material may be cut along line 60 priorto attachment to the header pan 52. This may be done, for example, toprovide a smooth lower face 62 if the header pan 52 is to be attached tothe lower face 62 rather than the sides 64 of the block of pottingmaterial 50. Cutting the potting material 50 may also be done whenrequired to re-open the ends 16, of the membranes 12, for example if alower layer 22 of adhesive 20 were not used in a modified mold used tocreate a cavity extending from the first layer 18 of adhesive 20 tobeyond the ends 16 of the membranes 12.

FIG. 4 shows a second mold 70. The second mold 70 is similar to thefirst mold 30 except that one set of contact surfaces 36 have beenconfigured to accept a pre-made header pan 52. The bundle 24 ofmembranes 12 is inserted into the header pan 52 such that the bottom ofthe second layer 22 of adhesive 20 is below the top edge of the headerpan 52, while the bottom of the first layer 18 of adhesive 20 is abovethe top edge of the header pan 52. When the plates 32, 34 are movedtogether, a set of contact surfaces compresses and temporarily sealsagainst the first layer 18 of adhesive 20 while another set of contactsurfaces 36 presses and temporarily seals against the permeate pan 52which in turn compresses and seals against the second layer 22 ofadhesive 20. This forms a cavity 44 including the potting area 14 and aregion at the top the permeate pan 52. The region at the top of thepermeate pan 52 may be inside permeate pan 52 outside the permeate pan52, or both. When the molten potting material is injected, the pottingmaterial flows between and around the membranes 12 and, when cooled to asolid, seals the membranes 12 relative to each other and to the permeatepan 52.

Injection molding of the potting material as described above can be doneat applied pressures in the range from 1-300 bar at temperatures from20-340° C. or 160-340° C. The potting material should remain a solid ofsufficient strength in all intended applications, which could involvecontact with fluids of up to 60° C. or more. Sample characteristics ofthe hot melt glue and the potting material are given below: Hotmelt Melttemperature 140-300° C. Strength (Utimate) 1-4 Mpa Hardness (Shore “A”)Over 40 shore “A” MFI (g/10 min at melting temperature) 100-1000 g/10min Potting Material Melt temperature 160-340° C. Strength (Utimate)10-150 Mpa Tensile Modulus Over 500 Mpa Hardness (Shore “A”) Over 50shore “A” MFI (g/10 min at melting temperature) 5-1000 g/10 min

For example, membranes 12, as used in ZEEWEED™ 500 series modules byZenon Environmental Inc. were potted in a first mold 30 using 3 types ofpolypropylene, having melt flow indexes between about 10 g/10 min and1000 g/10 min. Satisfactory results were obtained in potting bundles 24having 14 sheets 10 of membranes 12 using temperatures between 195 and230° C. and injection pressures between 90 and 110 bar. FIG. 6 shows onesuch potted bundle 24 cut through the polypropylene potting material 50.FIG. 7 is a photograph of the exterior of another such bundle.

The invention may be practiced with many variations from the embodimentsdescribed above without departing from the scope of the invention. Forexample, but without limitation, the invention may be used with tubularmembranes.

1. A hollow fiber membrane module wherein the membranes are pottedentirely in one or more thermoplastic materials that is/are solid atoperating temperatures of the module but was/were applied at atemperature above its/their melting point.
 2. The module of claim 1wherein the thermoplastic materials comprise a hot melt type material ina first region and an injection molding polymer in a second regionadjacent the first region, the injection molding material having ahigher strength and melt temperature than the hot melt type material. 3.The module of claim 1 wherein at least one of the thermoplasticmaterials has a melt temperature of greater than 140° C.
 4. A method ofpotting hollow fiber membranes comprising the steps of: a) forming abundle of hollow fiber membranes, the membranes held together by a layerof adhesive material spaced from the ends of the membranes to provide apotting region between the layer of adhesive material and the ends ofthe membranes; b) placing the bundle of membranes in a mold wherein themold seals against the adhesive material to form a cavity surround thepotting region; c) injecting a liquid potting material into the cavitysuch that the potting material flows around the membranes; d)solidifying the potting material in a seal with the membranes; and, e)removing the bundle of membranes from the mold.
 5. The method of claim 4wherein the potting material is a thermoplastic material that is madeliquid by melting it and solidified by cooling it.
 6. The method ofclaim 4 wherein the bundle is formed with a second layer of adhesivematerial on the opposite side of the potting region from the firstmaterial, and the cavity is formed in part by the second layer ofadhesive material.
 7. The method of claim 4 wherein the solidifiedpotting material is cut across the fibers to provide a face of thepotting material having open ends of the membranes flush with the face.8. The method of claim 6 wherein the cavity is formed in part by themold sealing against the second layer of adhesive material.
 9. Themethod of claim 6 wherein the cavity is formed in part by the moldsealing against a permeate pan surrounding the ends of the membranes andthe permeate pan sealing against the second layer of adhesive, thecavity arranged to also include a part of the surface of the walls ofthe permeate pan.
 10. The method of claim 4 further comprising sealingthe potting material to a permeate pan to form a fluid cavity in thepermeate pan in communication with the ends of the membranes.
 11. Themethod of claim 4 wherein the step of forming the bundle of membranes instep (a) of claim 4 further comprises providing a sheet of membranes andplacing a layer of hot melt adhesive over the sheet of membranes. 12.The method of claim 11 further comprising a step of stacking a pluralityof the sheets of claim 11 with their respective adhesive layers on topof each other.
 13. A bundle of potted hollow fiber membranes comprising:a) an array of hollow fiber membranes; b) a layer of adhesivesurrounding and connecting the membranes; and, c) a layer of athermoplastic polymer sealed to and between the membranes, wherein thelayer of thermoplastic polymer extends from the layer of adhesive to apoint at or spaced from the ends of the membranes.
 14. The bundle ofpotted membranes of claim 13 further comprising a second layer ofadhesive surrounding and connecting the membranes, the second layer ofadhesive extending from the layer of thermoplastic polymer to a point ator near the ends of the membranes.
 15. The bundle of potted membranesaccording to claim 13 wherein the layer of thermoplastic polymer isattached to a header pan to create a sealed fluid cavity within thepermeate pan, the ends of the membranes being open to the permeatecavity.